Pemanfaatan Limbah Pecahan Keramik Dan Kapur Sebagai Bahan Pengganti Sebagian Semen Pada Produksi Paving Blok Ditinjau Dari Nilai Kuat Tekan Dan Penyerapan Air

  • Aldi Setiawan Universitas Madura
  • Mohammad Saifuddin Teknik Sipil, Fakultas Teknik, Universitas Madura
  • Ragil Arman Maulana Teknik Sipil, Fakultas Teknik, Universitas Madura
Abstract views: 174 , PDF downloads: 253
Keywords: Ceramic shards, Limestone, Paving Blok

Abstract

Along with the rapid development of neighborhood and residential roads in Pamekasan, it has an impact on increasing the use of paving bloks for roads and residential yards. With the large number of needs, it has an impact on the need for paving blok materials, namely cement and aggregate, so a substitute material is needed to reduce dependence on the use of the main material. One of the substitute materials that can be used is the utilization of ceramic and lime waste which has not been used so far. The use of crushed ceramic shards and lime as a partial replacement of cement is expected to have an effect on the compressive strength of paving bloks. Utilization of ceramic and lime shard waste is expected to provide the latest innovations in the world of construction going forward. In this test, it is planned to pave a rectangular blok measuring 21x10.5x6 cm, and tested at the age of 7 days and 28 days on each variation of the mixture. %, and 25% replacement of cement with ceramics and lime. From the results of testing the chemical content of ceramics, it was found that the lime (CaO) content was 5.95% and the chemical content of the lime was found to have a lime (CaO) content of 50.84%. The results of the compressive test for each variation resulted in an increase in compressive strength from each variation. The greatest addition of compressive strength was found in the 20% variation with the resulting compressive strength of 30.35 Mpa at the age of 7 days, and 31.18 Mpa at the age of 28 days.

References

Putri, AZ., dan Imastuti (2017). “Pengaruh Penambahan Pecahan Keramik Pada Pembuatan Paving Blok Ditinjau Dari Nilai Kuat Tekan”. Jurnal Teknik Sipil Unika Soegijapranata G-Smart, Vol. 1 No. 1.
Mughni, MA., Siswanto, B., dan Agustin, RS. (2020).”Pengaruh Limbah Batu Kapur Kabupaten Lamongan Sebagai Pengganti sebagian Agregat Halus Terhadap Kuat Tekan Dan Penyerapan Air Paving Blok”. Indonesian Journal Of Civil Engineering Education Vol. 6 No. 2.
HA., Haris, A., Sambodj, SR., dan Aditya Febri (2017). “Pengaruh Penggunaan Abu Batu Terhadap Kuat Tekan Beton”. Institut Teknologi Adhi Tama Surabaya, Surabaya.
Purnama, SA., dan Sudibyo, T. (2018). “Pengaruh Limbah Keramik dan Abu Terbang Terhadap Kuat Tekan dan Daya Serap Air Bata Beton”. Jurnal Teknik Sipil dan Lingkungan Vol. 3 No. 3. Institut Pertanian Bogor.
Wahyuningtias, A., dan Khatulistiani, U. (2021). “Kekuatan Paving Blok Menggunakan Campuran Abu Sekam Padi Dan Kapur”. axial, Jurnal Rekayasa dan Manajemen Konstruksi Vol. 9, No.2. Univrsitas Wijaya Kusuma Surabaya.
Basuki, I., Lubis, MF., dan Daulay, MA. (2019). “Paving Blok Berbasis Abu Gosok”. Jurnal Pendidikan Teknik Bangunan dan Sipil Vol. 5, No.1.
Published
2023-03-30
How to Cite
Aldi Setiawan, Saifuddin, M., & Maulana, R. A. (2023). Pemanfaatan Limbah Pecahan Keramik Dan Kapur Sebagai Bahan Pengganti Sebagian Semen Pada Produksi Paving Blok Ditinjau Dari Nilai Kuat Tekan Dan Penyerapan Air. Ge-STRAM: Jurnal Perencanaan Dan Rekayasa Sipil, 6(1), 54-59. https://doi.org/10.25139/jprs.v6i1.5680
Section
Articles